Yttria-Stabilized Zirconia 8-10% 600-800MPa Flexural Strength ISO 6872 Certified Dental CAD/CAM

Name: YttriaStabilized Zirconia 810 600800MPa Flexural Strength ISO 6872 Certified Dental CADCAM
Brand: LEOTECH
Price: 56.94 USD

Wholesale Yttria-Stabilized Zirconia 8-10% 600-800MPa Flexural Strength ISO 6872 Certified Dental CAD/CAM from china suppliers

Brand Name : LEOTECH

Model Number : UT-ML

Certification : CE

Place of Origin : Chongqing, China

MOQ : 500 pcs

Price : 56.94

Payment Terms : T/T

Product Name : UT-ML Dental Zirconia Block

Product Specification : 98, 95, 92*75*25 mm

Thickness : 25 mm

Power Source : Manual

Warranty : 1 Year

After-sale Service : Online technical support

Quality Certification : FDA

Instrument classification : Class II

Contact Now

Yttria-Stabilized Zirconia (8-10%) 600-800MPa Flexural Strength ISO 6872 Certified Dental CAD/CAM

UT-ML Dental Zirconia Block

● Exceptional Mechanical Resilience
● Advanced Optical Clarity
● True-to-Nature Aesthetics

Yttria-Stabilized Zirconia 8-10% 600-800MPa Flexural Strength ISO 6872 Certified Dental CAD/CAM

Key Selling Points of UT-ML Zirconia
✅ Aesthetics: 49–53% translucency (1 mm)
✅ Strength: 800 MPa flexural strength
✅ Safety: 0 cytotoxicity | <0.1 Bq/g radioactivity
✅ Efficiency: 1500°C sintering (low-energy)
✅ Applications: Crowns & 3-unit bridges

Product Parameters:

Model	UT Multilayer 95mm
Size	95mm
Strength	600-800 MPa
Shades	16 VITA Classical.
Disc Sizes	9 thicknesses(10,12.14.16.18.20.22.25.30mm)

Technical Parameters:

1.Chemical composition

Components	UT-ML
ZrO2+HfO2+Y2O3	≥99%
Y2O3	8.0%-10.0%
Al2O3	＜0.15%
Other Oxides	＜0.5%

2.Physical characteristics

Properties	UT-ML
Density before sintering(g.cm-3)	3.15±0.05
Density after sintering(g.cm-3)	6.06±0.02
CTE(25-500℃)(K-1)	(10.5±0.5)×10-6
Flexural strength after sintering(Mpa)	600-800
Translucency(1.0±0.02mm)	49%-53%
Fracture toughness(MPa.m1/2)	3.5-5.0
Hardness(HV10)	1150-1250
Accelerated aging surface monoclinic phase content	＜5%
Chemical solubility after sintering(μg.cm-2)	＜100
Cytotoxicity	0 Level
Radioactivity(Bq.g-1)	＜0.1
Sintering temperature(℃)	1480-1510 Recommend 1500

Indications For Use ≤3 units

Yttria-Stabilized Zirconia 8-10% 600-800MPa Flexural Strength ISO 6872 Certified Dental CAD/CAM

Sintering:

Factory Display:

Application:

Exhibition:

Product Tags:

Yttria-Stabilized Zirconia 8-10% 600-800MPa Flexural Strength ISO 6872 Certified Dental CAD/CAM Images

Inquiry Cart 0

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Chongqing Leomed Technology Co., Ltd.
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!

Yttria-Stabilized Zirconia 8-10% 600-800MPa Flexural Strength ISO 6872 Certified Dental CAD/CAM

Yttria-Stabilized Zirconia 8-10% 600-800MPa Flexural Strength ISO 6872 Certified Dental CAD/CAM

600-800MPa Yttria Stabilized Zirconia

ISO 6872 Yttria Stabilized Zirconia

8-10% Yttria Stabilized Zirconia

Yttria-Stabilized Zirconia 8-10% 600-800MPa Flexural Strength ISO 6872 Certified Dental CAD/CAM Images