Dental Zirconia Blank UT-ML Grade 600-800MPa Strength & 49-53% Translucency for Crown/Bridge

Name: Dental Zirconia Blank UTML Grade 600800MPa Strength amp 4953 Translucency for CrownBridge
Brand: LEOTECH
Price: 28.47 USD

Wholesale Dental Zirconia Blank UT-ML Grade 600-800MPa Strength & 49-53% Translucency for Crown/Bridge from china suppliers

Brand Name : LEOTECH

Model Number : UT-ML

Certification : CE

Place of Origin : Chongqing, China

MOQ : 500 PCS

Price : 28.47

Payment Terms : T/T

Product Name : UT-ML Dental Zirconia Block

Product Specification : 98, 95, 92*75*10 mm

Thickness : 10 mm

Power Source : Manual

Warranty : 1 Year

After-sale Service : Online technical support

Shelf Life : 1 year

Quality Certification : ce

Instrument classification : Class II

Contact Now

Dental Zirconia Blank UT-ML Grade 600-800MPa Strength & 49-53% Translucency for Crown/Bridge

UT-ML Dental Zirconia Block

● High Strength ● High Transparency ● Natural

Dental Zirconia Blank UT-ML Grade 600-800MPa Strength & 49-53% Translucency for Crown/Bridge

UT-ML Multilayer Aesthetic Zirconia

Composition: ≥99% $ZrO2 + HfO2 + Y2 O3$ (8.0–10.0% $Y2 O3$ )
Density: 6.06 ± 0.02 g/cm³ (sintered)
Flexural Strength: 600–800 MPa | Translucency: 49–53% (1.0 mm)
Recommended Use: Single crowns & ≤3-unit bridges
Sintering: 1500°C (1480–1510°C range)

Technical Parameters:

1.Chemical composition

Components	UT-ML
ZrO2+HfO2+Y2O3	≥99%
Y2O3	8.0%-10.0%
Al2O3	＜0.15%
Other Oxides	＜0.5%

2.Physical characteristics

Properties	UT-ML
Density before sintering(g.cm-3)	3.15±0.05
Density after sintering(g.cm-3)	6.06±0.02
CTE(25-500℃)(K-1)	(10.5±0.5)×10-6
Flexural strength after sintering(Mpa)	600-800
Translucency(1.0±0.02mm)	49%-53%
Fracture toughness(MPa.m1/2)	3.5-5.0
Hardness(HV10)	1150-1250
Accelerated aging surface monoclinic phase content	＜5%
Chemical solubility after sintering(μg.cm-2)	＜100
Cytotoxicity	0 Level
Radioactivity(Bq.g-1)	＜0.1
Sintering temperature(℃)	1480-1510 Recommend 1500

Indications For Use ≤3 units

Dental Zirconia Blank UT-ML Grade 600-800MPa Strength & 49-53% Translucency for Crown/Bridge

Sintering:

Factory Display:

Application:

Exhibition:

Product Tags:

Dental Crown Zirconia Blank

UT ML Dental Zirconia Blank

Bridge Dental Zirconia Blank

Dental Zirconia Blank UT-ML Grade 600-800MPa Strength & 49-53% Translucency for Crown/Bridge Images

Inquiry Cart 0

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Chongqing Leomed Technology Co., Ltd.
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!